The Right Formulation for All of Your Coating Needs

11000 Series Highest Exterior Performance Organic Systems are formulated to meet the requirments of the AAMA 2605 specification. Products in this series have a 60° gloss range of 25-35% and are available in a wide selection of colors . Propeamorphous chromium phosphate or amourphous chromate pretreatmentis critical for product performance. The chrome coating weight must be applied at 40 mg/ft2 minimum. A TCI technical representative must audit each application to insure products will meet the 2605 specification.

Characteristic ASTM # # Result
Specific Gravity D-792 1.4 to 1.9 depending on color.
Theoretical Coverage Approximately 101 to 138 ft2 / lb. / mil.
Optimum Storage <80° F, < 50%RH
Particle Distribution +44 microns (325 mesh) Percentage varies with color
Film Thickness D-1186 1 to 3 mils.
Percent Gloss @ 60° D-523-89 25 to 35%
Pencil Hardness D-3363-00 H to 2H
Adhesion D-3359-02 No lifting of 1/8" squares between scribed lines when
cross hatch adhesion is tested using the prescribed tape.
Flexibility D-522-93a A coating of 2 mils or less will withstand a bend of 180°
over a 1/8" mandrel without cracking or loss of adhesion.
Impact Resistance D-2794-93 100 inch-pounds, direct and reverse, at a film thickness of 2 mils.
Impact properties will be influenced by formulation.
Salt Spray Resistance B-117-97 Minimum rating of 7 for procedure A and minimum of 8 for procedure B (ASTM-D-1654-92) after
4000 hours of exposure. Aluminum substrates must be pretreated according to AAMA 2605 specs.
Humidity Resistance D-2247 No more than "few" blisters size 8, figure #4, ASTM-D-714 after 4000 hours of exposure.
Aluminum substrates must be pretreated according to AAMA 2605specs.
Chemical Resistance Very good resistance to most chemicals and solvents.
See AAMA 2605 chemical resistance requirements.
Some properties may be reduced in low gloss formulations.
Overbake Stability Excellent.